Stainless steel tee‘s hydraulic bulging process is through the metal materials of axial compensation bulge out a kind of branch pipe forming process.
The process is to use special hydraulic press, with three links within the tube billet diameter equal injection liquid, through the two horizontal side of the hydraulic cylinder synchronization of the motion of tube billet, billet after squeezed smaller volume, smaller volume of liquid with the tube billet inside the tube billet and the pressure increases, when the stainless steel tee’s branch pipe bulge out to the pressure, the metal material in the liquid in the cylinder and the pipe pressure under the dual role of flow along the mold cavity and the branch pipe.
Stainless steel tee hydraulic bulging process can be a forming, high production efficiency; Stainless steel tee head and shoulders of wall thickness are increased.
Stainless steel tee:
By the hydraulic bulging process equipment for stainless steel tee tonnage is larger, the current domestic is mainly used for less than the standard of DN400 wall thickness in the manufacturing of stainless steel tee. Its applicable forming material for cold hardening tend to be relatively low low carbon steel, low alloy steel, stainless steel, including some non-ferrous metal materials, such as copper, aluminum, titanium, etc.
Tuesday, January 4, 2022
The hydraulic bulge forming technology of stainless steel tee
Related Posts:
Duplex Stainless Steel Group By wilsonpipeline.comDuplex Stainless Steel Group is intermediate in terms of structure and alloy content between ferritic and austenitic stainless steel. The main charact… Read More
Composition Effect Magnetic Permeability of Austenitic Stainless Steel By wilsonpipeline.comAustenitic stainless steel are generally non-magnetic with magnetic permeabilities of around 1.0. Permeabilities above 1.0 are associated with the amo… Read More
Effect of Cold Work and Heat Treatment of Austenitic Stainless Steel By wilsonpipeline.com Austenitic stainless steel are generally non magnetic with magnetic permeabilities of around 1.0. Permeabilities above 1.0 are associated with the am… Read More
Martensitic and Precipitation Austenitic Stainless Steel Comparison Table By wilsonpipeline.comMartensitic and Precipitation Austenitic Stainless Steel Comparison Table is intended to relate former BS, EN, German and Swedish grade designations t… Read More
Martensitic Stainless Steel By wilsonpipeline.comMartensitic stainless steel have the highest strength but also the lowest corrosion resistance of the stainless steel. Martensitic steels with high ca… Read More
Standard Reference for Seamless Steel Pipe
1. Seamless steel tube for structure (GB / T8162-1999) is a seamless steel pipe for general structure and mechanical structure. 2. Seamles...

0 comments:
Post a Comment