Stainless Steel 410

Stainless steel 410 is a basic martensitic grade which contains 11.5% chromium, offering both exceptional wear and corrosion resistance. Stainless steel 410 is corrosion resistant to some chemicals, food, mild acids, water, and air. It also proves adequate resistance to nitric acid, concentrated sulfuric acid, dilute acetic acid and naphtha. Elevated mechanical properties and corrosion resistance are achieved with stainless steel 410 when it’s hardened and tempered. 

Stainless steel 410 is used in applications such as dental and surgical instruments, pipelines, valves and nozzles, automotive parts and more.Stainless steel 410 is generally used for applications which involve mild corrosion, high strength, and heat resistance.  Please contact wilsonpipeline Pipe Industry for more information about stainless steel 410, its properties, and its applications.

Heat Treatment:

Galvanizing: Heat slowly to 1500 -1650°F, cool to 1100°F in furnace, air cool. Process Galvanizing: Heat to 1350 -1450°F, air cool. Hardening: Heat to 1700 – 1850°F, air cool or oil quench. Follow by temper or stress-relief. Stress Relieving: Heat at 300 – 800°F for 1 to 2 hours, air cool. See our stainless steel heat treating services.

Forming:

Stainless steel 410 has cold working properties which allow it to be temperately drawn and shaped in the galvanized condition.

Fabrication:

The martensitic alloys offer unique hardening capabilities which limit their capability of being welded using conventional techniques. Stainless steel 410must first be pre-heated, followed by a post-weld galvanizing treatment to alleviate cracking.

Stainless steel 410 Standards

  • UNS S41000
  • ASTM A182
  • ASTM A276
  • ASTM A479

Composition (%)

  • Carbon 0.080-0.150
  • Chromium 11.50-13.50
  • Manganese 1.0 Max
  • Phosphorus 1.0 Max
  • Silicon 1.00 Max
  • Sulfur 0.030 Max

Applications

  • Pump Shafts
  • Valve Components
  • Gas and Steam Turbine Components

Stainless Steel 410 Flanges Stock

  • Blind Flanges
  • Lap Joint Flanges
  • Weld Neck Flanges
  • Slip On Flanges
  • Plate Flanges

Stainless Steel 410 Pipes Stock

Stainless Steel 410 Pipe Fittings Stock

Stainless Steel 410 Mechanical Properties

Material TypeConditionUltimate Tensile Strength (PSI)0.2% Yield Strength (PSI)Elongation (% In 2in.)Reduction Of Area (%)Hardness BrinellHardness Rockwell
Stainless steel 410T100,00080,0001240**
 H120,00090,0001240**
 Annealed70,00040,0001645**
 Class2110,00085,0001545269 Max*
 NACE MRO 175*****22 HRC Max

Our website: www.wilsonpipeline.com . Please send your detailed requirements to sales@wilsonpipeline.com. We will give you the best offer.

Related Posts:

  • What is a lens ring joint gasketlens ring joint gasket is a line contact seal for use in high pressure piping systems and in pressure vessel heads. The lens cross section is a spheri… Read More
  • What is a ring joint gasketRing Joint Gasket is widely used in oil, petroleum and chemical process fields. Precision machined, metallic sealing rings suitable for high pressure … Read More
  • What is a jacket gasketJacket gasket with soft pliable core, surrounded by a metal jacket that totally or partially encloses the filler material. Partition bars can be incor… Read More
  • What is a solid copper gasketSolid copper gasket to make a leak tight UHV seal between two conflat flanges. Oxygen free high conductivity (OFHC) copper is normally used as this se… Read More
  • what is a graphite gasketGraphite Gasket that it is made from graphite as homogeneous, reinforced by metal mesh, foil or tanged metal. Graphite gaskets is widely used for pipe… Read More

0 comments:

Post a Comment

Standard Reference for Seamless Steel Pipe

 1. Seamless steel tube for structure (GB / T8162-1999) is a seamless steel pipe for general structure and mechanical structure. 2. Seamles...