Stainless Steel 410 Material Property Data By wilsonpipeline.com

Stainless Steel 410 is the general purpose and most widely used of all the Martensitic grades of stainless steels. In its annealed condition it may be drawn, formed or shaped and because it is an air or oil quench hardening grade it can be hardened to high strength levels by subsequent heat treatments. While Stainless Steel 410 offers very good resistance to scaling up to 1200° F., and its mechanical properties are excellent, it is NOT recommended for applications in which severe corrosion is encountered. 

Stainless Steel 410 is used for springs, scrapers, fasteners, hardware brackets, furnace parts and burners. It is magnetic in all conditions. Tensile strength (as annealed) min. 65,000 PSI, yield strength minimum 30,000 PSI, and elongation in 2 inches at 20%. For solution annealing, slow controlled cooling from 1500/1600° F. For hardening, heat to 1700/1850°F. Quench in air or oil.

The following specifications cover Stainless Steel 410

  • AISI 410
  • AMS 5504
  • AMS 5505
  • AMS 5591
  • AMS 5613
  • AMS 5776
  • ASTM A176
  • ASTM A182 (F6A, F8a)
  • ASTM A193 (410,B6, B6X)
  • ASTM A194 (410,B6, B6X)
  • ASTM A240
  • ASTM A268
  • ASTM A276
  • ASTM A314
  • ASTM A336
  • ASTM A473
  • ASTM A479
  • ASTM A493
  • ASTM A511
  • ASTM A580
  • DIN 1.4006
  • UNS S41000

Related Metals:

  • AF 410QDT(tm)

Chemistry Data : 

Carbon

0.15 max

Chromium

11.5 – 13.5

Iron

Balance

Manganese

1 max

Phosphorus

0.04 max

Silicon

1 max

Sulphur

0.03 max

Principal Design FeaturesStainless Steel 410 is the basic martensitic stainless which will attain high mechanical properties after heat treatment. It has good impact strength, corrosion and scaling resistance up to 1200 F (649 C).
ApplicationsCutlery, steam and gas turbine blades and buckets, bushings, valve components,stainless steel 410 pipes, stainless steel 410 tubes, stainless steel 904L fittings, stainless steel 410 flanges, fasteners, screens and kitchen utensils.
MachinabilityTough, draggy chips with heavy build-up. While this alloy can be machined in the annealed condition, it tends to perform better in the cold drawn or heat treated condition.
WeldingMost common methods of welding can be successfully employed with this alloy. To reduce the chance of cracking, it is advisable to preheat the workpiece to 350-400 F (177-204 C). Post-weld annealing is recommended to reattain maximum ductility. Filler metal, when required, should be AWS E/ER410.
Hot Working2000-2200 F (1093-1204 C) is the proper hot work range. Do not work this material below 1650 F (899 C).
Cold WorkingReadily cold formed using most of the common practices.
Annealing1200-1400 F (649-760 C), followed by air cooling.
TemperingTemper for desired hardness, air or furnace cool.
Hardening1750-1850 F (954-1010 C), oil quench for maximum hardness.

Physical Data : 

Density (lb / cu. in.)0.28
Specific Gravity7.7
Specific Heat (Btu/lb/Deg F – [32-212 Deg F])0.11
Electrical Resistivity (microhm-cm (at 68 Deg F))342
Melting Point (Deg F)2790
Modulus of Elasticity Tension29

wilsonpipeline is a supplier of stainless steel 410 pipes, stainless steel 410 tubes, stainless steel 904L fittings, stainless steel410 forgings, stainless steel 410 flanges, and stainless steel 410 fasteners including; stainless steel 410 nuts, stainless steel410 bolts and more.

Source: wilsonpipeline Pipe Industry (www.wilsonpipeline.com)

Related Posts:

  • Reducing TeeA Reducing Tee is also called “unequal tee“, which means the tee branch pipe diameter is not same with the run pipe of the tee. Commonly, in a reducin… Read More
  • Equal TeeWhat is equal teeEqual tee, means the branch diameter of this tee is same with the main pipe (Run pipe) diameter of this tee. When we see only one siz… Read More
  • Pipe CrossPipe cross is also called cross fitting ,it looks like tee but has four ends. Think about a new branch pass through a equal tee, it is a cross . Commo… Read More
  • Equal CrossEqual CrossThe equal cross is one kind of the pipe cross, just like a equal tee, the equal cross means all the 4 ends of the cross are in same diamete… Read More
  • Reducing crossReducing crossThe reducing cross also is called unequal pipe cross , it is the pipe cross which the four branch ends are not in the same diameters.  j… Read More

0 comments:

Post a Comment

Standard Reference for Seamless Steel Pipe

 1. Seamless steel tube for structure (GB / T8162-1999) is a seamless steel pipe for general structure and mechanical structure. 2. Seamles...